A13B2C2_oP34_32_a6c_c_c & a,b/a,c/a,z1,x2,y2,z2,x3,y3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6,x7,y7,z7,x8,y8,z8,x9,y9,z9 --params=8.4261784988,1.1450866366,0.701103726564,0.0,0.808,0.55,0.8946,0.614,0.7595,-0.0255,0.8197,0.8044,0.642,0.5367,0.6481,0.3894,0.7689,-0.0703,0.2917,0.8392,0.688,0.2793,0.67666,0.60773,0.0844,0.8643,0.8235,0.4147 & Pba2 C_{2v}^{8} #32 (ac^8) & oP34 & None & Re2O5[SO4]2 & & U. Betke and M. S. Wickleder, Inorg. Chem. 50, 858-872 (2011) 1.00000000000000 8.42617849880000 0.00000000000000 0.00000000000000 0.00000000000000 9.64870439660000 0.00000000000000 0.00000000000000 0.00000000000000 5.90762514620000 O Re S 26 4 4 Direct 0.00000000000000 0.00000000000000 0.00000000000000 O (2a) 0.50000000000000 0.50000000000000 0.00000000000000 O (2a) 0.80800000000000 0.55000000000000 0.89460000000000 O (4c) -0.80800000000000 -0.55000000000000 0.89460000000000 O (4c) 1.30800000000000 -0.05000000000000 0.89460000000000 O (4c) -0.30800000000000 1.05000000000000 0.89460000000000 O (4c) 0.61400000000000 0.75950000000000 -0.02550000000000 O (4c) -0.61400000000000 -0.75950000000000 -0.02550000000000 O (4c) 1.11400000000000 -0.25950000000000 -0.02550000000000 O (4c) -0.11400000000000 1.25950000000000 -0.02550000000000 O (4c) 0.81970000000000 0.80440000000000 0.64200000000000 O (4c) -0.81970000000000 -0.80440000000000 0.64200000000000 O (4c) 1.31970000000000 -0.30440000000000 0.64200000000000 O (4c) -0.31970000000000 1.30440000000000 0.64200000000000 O (4c) 0.53670000000000 0.64810000000000 0.38940000000000 O (4c) -0.53670000000000 -0.64810000000000 0.38940000000000 O (4c) 1.03670000000000 -0.14810000000000 0.38940000000000 O (4c) -0.03670000000000 1.14810000000000 0.38940000000000 O (4c) 0.76890000000000 -0.07030000000000 0.29170000000000 O (4c) -0.76890000000000 0.07030000000000 0.29170000000000 O (4c) 1.26890000000000 0.57030000000000 0.29170000000000 O (4c) -0.26890000000000 0.42970000000000 0.29170000000000 O (4c) 0.83920000000000 0.68800000000000 0.27930000000000 O (4c) -0.83920000000000 -0.68800000000000 0.27930000000000 O (4c) 1.33920000000000 -0.18800000000000 0.27930000000000 O (4c) -0.33920000000000 1.18800000000000 0.27930000000000 O (4c) 0.67666000000000 0.60773000000000 0.08440000000000 Re (4c) -0.67666000000000 -0.60773000000000 0.08440000000000 Re (4c) 1.17666000000000 -0.10773000000000 0.08440000000000 Re (4c) -0.17666000000000 1.10773000000000 0.08440000000000 Re (4c) 0.86430000000000 0.82350000000000 0.41470000000000 S (4c) -0.86430000000000 -0.82350000000000 0.41470000000000 S (4c) 1.36430000000000 -0.32350000000000 0.41470000000000 S (4c) -0.36430000000000 1.32350000000000 0.41470000000000 S (4c)