A2B3C6_cP33_221_cd_ag_fh & a,x4,x5,x6 --params=7.624,0.3,0.2,0.2 & Pm-3m O_{h}^{1} #221 (acdfgh) & cP33 & $E9_{1}$ & Ca3Al2O6 & Ca3Al2O6 & F. A. Steele and W. P. Davey, J. Am. Chem. Soc. 51, 2283-2293 (1929) 1.00000000000000 7.62400000000000 0.00000000000000 0.00000000000000 0.00000000000000 7.62400000000000 0.00000000000000 0.00000000000000 0.00000000000000 7.62400000000000 Al Ca O 6 9 18 Direct 0.00000000000000 0.50000000000000 0.50000000000000 Al (3c) 0.50000000000000 0.00000000000000 0.50000000000000 Al (3c) 0.50000000000000 0.50000000000000 0.00000000000000 Al (3c) 0.50000000000000 0.00000000000000 0.00000000000000 Al (3d) 0.00000000000000 0.50000000000000 0.00000000000000 Al (3d) 0.00000000000000 0.00000000000000 0.50000000000000 Al (3d) 0.00000000000000 0.00000000000000 0.00000000000000 Ca (1a) 0.20000000000000 0.20000000000000 0.20000000000000 Ca (8g) -0.20000000000000 -0.20000000000000 0.20000000000000 Ca (8g) -0.20000000000000 0.20000000000000 -0.20000000000000 Ca (8g) 0.20000000000000 -0.20000000000000 -0.20000000000000 Ca (8g) 0.20000000000000 0.20000000000000 -0.20000000000000 Ca (8g) -0.20000000000000 -0.20000000000000 -0.20000000000000 Ca (8g) 0.20000000000000 -0.20000000000000 0.20000000000000 Ca (8g) -0.20000000000000 0.20000000000000 0.20000000000000 Ca (8g) 0.30000000000000 0.50000000000000 0.50000000000000 O (6f) -0.30000000000000 0.50000000000000 0.50000000000000 O (6f) 0.50000000000000 0.30000000000000 0.50000000000000 O (6f) 0.50000000000000 -0.30000000000000 0.50000000000000 O (6f) 0.50000000000000 0.50000000000000 0.30000000000000 O (6f) 0.50000000000000 0.50000000000000 -0.30000000000000 O (6f) 0.20000000000000 0.50000000000000 0.00000000000000 O (12h) -0.20000000000000 0.50000000000000 0.00000000000000 O (12h) 0.00000000000000 0.20000000000000 0.50000000000000 O (12h) 0.00000000000000 -0.20000000000000 0.50000000000000 O (12h) 0.50000000000000 0.00000000000000 0.20000000000000 O (12h) 0.50000000000000 0.00000000000000 -0.20000000000000 O (12h) 0.50000000000000 0.20000000000000 0.00000000000000 O (12h) 0.50000000000000 -0.20000000000000 0.00000000000000 O (12h) 0.20000000000000 0.00000000000000 0.50000000000000 O (12h) -0.20000000000000 0.00000000000000 0.50000000000000 O (12h) 0.00000000000000 0.50000000000000 -0.20000000000000 O (12h) 0.00000000000000 0.50000000000000 0.20000000000000 O (12h)