A2B6C3_oP44_62_2c_2c2d_3c & a,b/a,c/a,x1,z1,x2,z2,x3,z3,x4,z4,x5,z5,x6,z6,x7,z7,x8,y8,z8,x9,y9,z9 --params=9.794,0.58627731264,1.3977945681,0.1324,0.4084,0.1792,0.736,0.8837,0.1626,0.3229,-0.0759,0.0298,0.1757,0.0907,0.0289,0.3015,0.0293,-0.0807,0.5411,0.779,0.6492,0.541,-0.076 & Pnma D_{2h}^{16} #62 (c^7d^2) & oP44 & $K5_{1}$ & K2O6S3 & K2O6S3 & J. M. Stewart and J. T. Szyma\'{n}ski, Acta Crystallogr. Sect. B Struct. Sci. 35, 1967-1970 (1979) 1.00000000000000 9.79400000000000 0.00000000000000 0.00000000000000 0.00000000000000 5.74200000000000 0.00000000000000 0.00000000000000 0.00000000000000 13.69000000000000 K O S 8 24 12 Direct 0.13240000000000 0.25000000000000 0.40840000000000 K (4c) 0.36760000000000 0.75000000000000 0.90840000000000 K (4c) -0.13240000000000 0.75000000000000 -0.40840000000000 K (4c) 0.63240000000000 0.25000000000000 0.09160000000000 K (4c) 0.17920000000000 0.25000000000000 0.73600000000000 K (4c) 0.32080000000000 0.75000000000000 1.23600000000000 K (4c) -0.17920000000000 0.75000000000000 -0.73600000000000 K (4c) 0.67920000000000 0.25000000000000 -0.23600000000000 K (4c) 0.88370000000000 0.25000000000000 0.16260000000000 O (4c) -0.38370000000000 0.75000000000000 0.66260000000000 O (4c) -0.88370000000000 0.75000000000000 -0.16260000000000 O (4c) 1.38370000000000 0.25000000000000 0.33740000000000 O (4c) 0.32290000000000 0.25000000000000 -0.07590000000000 O (4c) 0.17710000000000 0.75000000000000 0.42410000000000 O (4c) -0.32290000000000 0.75000000000000 0.07590000000000 O (4c) 0.82290000000000 0.25000000000000 0.57590000000000 O (4c) -0.08070000000000 0.54110000000000 0.77900000000000 O (8d) 0.58070000000000 -0.54110000000000 1.27900000000000 O (8d) 0.08070000000000 1.04110000000000 -0.77900000000000 O (8d) 0.41930000000000 -0.04110000000000 -0.27900000000000 O (8d) 0.08070000000000 -0.54110000000000 -0.77900000000000 O (8d) 0.41930000000000 0.54110000000000 -0.27900000000000 O (8d) -0.08070000000000 -0.04110000000000 0.77900000000000 O (8d) 0.58070000000000 1.04110000000000 1.27900000000000 O (8d) 0.64920000000000 0.54100000000000 -0.07600000000000 O (8d) -0.14920000000000 -0.54100000000000 0.42400000000000 O (8d) -0.64920000000000 1.04100000000000 0.07600000000000 O (8d) 1.14920000000000 -0.04100000000000 0.57600000000000 O (8d) -0.64920000000000 -0.54100000000000 0.07600000000000 O (8d) 1.14920000000000 0.54100000000000 0.57600000000000 O (8d) 0.64920000000000 -0.04100000000000 -0.07600000000000 O (8d) -0.14920000000000 1.04100000000000 0.42400000000000 O (8d) 0.02980000000000 0.25000000000000 0.17570000000000 S (4c) 0.47020000000000 0.75000000000000 0.67570000000000 S (4c) -0.02980000000000 0.75000000000000 -0.17570000000000 S (4c) 0.52980000000000 0.25000000000000 0.32430000000000 S (4c) 0.09070000000000 0.25000000000000 0.02890000000000 S (4c) 0.40930000000000 0.75000000000000 0.52890000000000 S (4c) -0.09070000000000 0.75000000000000 -0.02890000000000 S (4c) 0.59070000000000 0.25000000000000 0.47110000000000 S (4c) 0.30150000000000 0.25000000000000 0.02930000000000 S (4c) 0.19850000000000 0.75000000000000 0.52930000000000 S (4c) -0.30150000000000 0.75000000000000 -0.02930000000000 S (4c) 0.80150000000000 0.25000000000000 0.47070000000000 S (4c)