A3B2_oP20_56_ce_e & a,b/a,c/a,z1,x2,y2,z2,x3,y3,z3 --params=4.911,2.53797597231,1.10201588271,0.029,0.147,0.058,0.861,0.044,0.128,0.179 & Pccn D_{2h}^{10} #56 (ce^2) & oP20 & D5_{11} & Sb2O3 & & C. Svensson, Acta Cryst. B 30, 458-461 (1974) 1.0000000000000000 4.91100000000000 0.00000000000000 0.00000000000000 0.00000000000000 12.46400000000000 0.00000000000000 0.00000000000000 0.00000000000000 5.41200000000000 O Sb 12 8 Direct 0.25000000000000 0.25000000000000 0.02900000000000 O (4c) 0.25000000000000 0.25000000000000 0.52900000000000 O (4c) 0.75000000000000 0.75000000000000 0.47100000000000 O (4c) 0.75000000000000 0.75000000000000 0.97100000000000 O (4c) 0.14700000000000 0.05800000000000 -0.13900000000000 O (8e) 0.14700000000000 0.44200000000000 0.36100000000000 O (8e) 0.35300000000000 0.05800000000000 0.36100000000000 O (8e) 0.35300000000000 0.44200000000000 -0.13900000000000 O (8e) 0.64700000000000 0.55800000000000 0.13900000000000 O (8e) 0.64700000000000 0.94200000000000 0.63900000000000 O (8e) 0.85300000000000 0.55800000000000 0.63900000000000 O (8e) 0.85300000000000 0.94200000000000 0.13900000000000 O (8e) 0.04400000000000 0.12800000000000 0.17900000000000 Sb (8e) 0.04400000000000 0.37200000000000 0.67900000000000 Sb (8e) 0.45600000000000 0.12800000000000 0.67900000000000 Sb (8e) 0.45600000000000 0.37200000000000 0.17900000000000 Sb (8e) 0.54400000000000 0.62800000000000 0.82100000000000 Sb (8e) 0.54400000000000 0.87200000000000 0.32100000000000 Sb (8e) 0.95600000000000 0.62800000000000 0.32100000000000 Sb (8e) 0.95600000000000 0.87200000000000 0.82100000000000 Sb (8e)