A3B5C4D2_mC56_9_3a_5a_4a_2a & a,b/a,c/a,beta,x1,y1,z1,x2,y2,z2,x3,y3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6,x7,y7,z7,x8,y8,z8,x9,y9,z9,x10,y10,z10,x11,y11,z11,x12,y12,z12,x13,y13,z13,x14,y14,z14 --params=5.34,1.73052434457,2.75074906367,93.66,0.8852,0.198,0.2303,0.3747,0.3771,0.2327,0.8818,0.5235,0.2204,0.0726,0.1978,0.0,0.2387,0.475,0.0023,0.7395,0.4214,0.0063,0.0438,0.3596,0.156,0.532,0.537,0.155,0.7299,0.363,0.2878,0.2395,0.197,0.2791,0.5334,0.2053,0.1807,0.2025,0.5416,0.296,0.0257,0.3641,0.041,0.5208,0.5335,0.04 & Cc C_{s}^{4} #9 (a^14) & mC56 & None & Mg3O5(OH)4Si2 & Chrysotile & G. Falini et al., Chem. Eur. J. 10, 3043-3049 (2004) 1.00000000000000 2.67000000000000 -4.62050000000000 0.00000000000000 2.67000000000000 4.62050000000000 0.00000000000000 -0.93768136424044 0.00000000000000 14.65904071415170 Mg O OH Si 6 10 8 4 Direct 0.68720000000000 1.08320000000000 0.23030000000000 Mg (4a) 1.08320000000000 0.68720000000000 0.73030000000000 Mg (4a) -0.00240000000000 0.75180000000000 0.23270000000000 Mg (4a) 0.75180000000000 -0.00240000000000 0.73270000000000 Mg (4a) 0.35830000000000 1.40530000000000 0.22040000000000 Mg (4a) 1.40530000000000 0.35830000000000 0.72040000000000 Mg (4a) -0.12520000000000 0.27040000000000 0.00000000000000 O (4a) 0.27040000000000 -0.12520000000000 0.50000000000000 O (4a) -0.23630000000000 0.71370000000000 0.00230000000000 O (4a) 0.71370000000000 -0.23630000000000 0.50230000000000 O (4a) 0.31810000000000 1.16090000000000 0.00630000000000 O (4a) 1.16090000000000 0.31810000000000 0.50630000000000 O (4a) -0.31580000000000 0.40340000000000 0.15600000000000 O (4a) 0.40340000000000 -0.31580000000000 0.65600000000000 O (4a) -0.00500000000000 1.06900000000000 0.15500000000000 O (4a) 1.06900000000000 -0.00500000000000 0.65500000000000 O (4a) 0.36690000000000 1.09290000000000 0.28780000000000 OH (4a) 1.09290000000000 0.36690000000000 0.78780000000000 OH (4a) 0.04250000000000 0.43650000000000 0.27910000000000 OH (4a) 0.43650000000000 0.04250000000000 0.77910000000000 OH (4a) 0.32810000000000 0.73870000000000 0.18070000000000 OH (4a) 0.73870000000000 0.32810000000000 0.68070000000000 OH (4a) -0.33910000000000 0.74410000000000 0.29600000000000 OH (4a) 0.74410000000000 -0.33910000000000 0.79600000000000 OH (4a) -0.33840000000000 0.38980000000000 0.04100000000000 Si (4a) 0.38980000000000 -0.33840000000000 0.54100000000000 Si (4a) -0.01270000000000 1.05430000000000 0.04000000000000 Si (4a) 1.05430000000000 -0.01270000000000 0.54000000000000 Si (4a)