A3BC_hP30_185_cd_c_ab & a,c/a,z1,z2,x3,z3,x4,z4,x5,y5,z5 --params=11.795090915,0.502416278086,0.0,0.377,0.1598,0.2396,0.6647,0.1706,0.1732,0.5056,0.1148 & P6_{3}cm C_{6v}^{3} #185 (abc^2d) & hP30 & None & KNiCl3 & & D. Visser and G. C. Verschoor and D. J. W. {IJdo}, Acta Crystallogr. Sect. B Struct. Sci. 36, 28-34 (1980) 1.00000000000000 5.89754545750000 -10.21484837233700 0.00000000000000 5.89754545750000 10.21484837233700 0.00000000000000 0.00000000000000 0.00000000000000 5.92604567720000 Cl K Ni 18 6 6 Direct 0.15980000000000 0.00000000000000 0.23960000000000 Cl (6c) 0.00000000000000 0.15980000000000 0.23960000000000 Cl (6c) -0.15980000000000 -0.15980000000000 0.23960000000000 Cl (6c) -0.15980000000000 0.00000000000000 0.73960000000000 Cl (6c) 0.00000000000000 -0.15980000000000 0.73960000000000 Cl (6c) 0.15980000000000 0.15980000000000 0.73960000000000 Cl (6c) 0.17320000000000 0.50560000000000 0.11480000000000 Cl (12d) -0.50560000000000 -0.33240000000000 0.11480000000000 Cl (12d) 0.33240000000000 -0.17320000000000 0.11480000000000 Cl (12d) -0.17320000000000 -0.50560000000000 0.61480000000000 Cl (12d) 0.50560000000000 0.33240000000000 0.61480000000000 Cl (12d) -0.33240000000000 0.17320000000000 0.61480000000000 Cl (12d) -0.50560000000000 -0.17320000000000 0.61480000000000 Cl (12d) 0.33240000000000 0.50560000000000 0.61480000000000 Cl (12d) 0.17320000000000 -0.33240000000000 0.61480000000000 Cl (12d) 0.50560000000000 0.17320000000000 0.11480000000000 Cl (12d) -0.33240000000000 -0.50560000000000 0.11480000000000 Cl (12d) -0.17320000000000 0.33240000000000 0.11480000000000 Cl (12d) 0.66470000000000 0.00000000000000 0.17060000000000 K (6c) 0.00000000000000 0.66470000000000 0.17060000000000 K (6c) -0.66470000000000 -0.66470000000000 0.17060000000000 K (6c) -0.66470000000000 0.00000000000000 0.67060000000000 K (6c) 0.00000000000000 -0.66470000000000 0.67060000000000 K (6c) 0.66470000000000 0.66470000000000 0.67060000000000 K (6c) 0.00000000000000 0.00000000000000 0.00000000000000 Ni (2a) 0.00000000000000 0.00000000000000 0.50000000000000 Ni (2a) 0.33333333333333 0.66666666666667 0.37700000000000 Ni (4b) 0.66666666666667 0.33333333333333 0.87700000000000 Ni (4b) 0.33333333333333 0.66666666666667 0.87700000000000 Ni (4b) 0.66666666666667 0.33333333333333 0.37700000000000 Ni (4b)