A3B_hP16_194_gh_ac & a,c/a,x4 --params=5.096,1.6295133438,-0.16667 & P6_{3}/mmc D_{6h}^{4} #194 (acgh) & hP16 & $D0_{24}$ & Ni3Ti & & F. Laves and H. J. Wallbaum, Zeitschrift f{\"u}r Kristallographie - Crystalline Materials 101, 78-93 (1939) 1.00000000000000 2.54800000000000 -4.41326545768550 0.00000000000000 2.54800000000000 4.41326545768550 0.00000000000000 0.00000000000000 0.00000000000000 8.30400000000000 Ni Ti 12 4 Direct 0.50000000000000 0.00000000000000 0.00000000000000 Ni (6g) 0.00000000000000 0.50000000000000 0.00000000000000 Ni (6g) 0.50000000000000 0.50000000000000 0.00000000000000 Ni (6g) 0.50000000000000 0.00000000000000 0.50000000000000 Ni (6g) 0.00000000000000 0.50000000000000 0.50000000000000 Ni (6g) 0.50000000000000 0.50000000000000 0.50000000000000 Ni (6g) -0.16667000000000 -0.33334000000000 0.25000000000000 Ni (6h) 0.33334000000000 0.16667000000000 0.25000000000000 Ni (6h) -0.16667000000000 0.16667000000000 0.25000000000000 Ni (6h) 0.16667000000000 0.33334000000000 0.75000000000000 Ni (6h) -0.33334000000000 -0.16667000000000 0.75000000000000 Ni (6h) 0.16667000000000 -0.16667000000000 0.75000000000000 Ni (6h) 0.00000000000000 0.00000000000000 0.00000000000000 Ti (2a) 0.00000000000000 0.00000000000000 0.50000000000000 Ti (2a) 0.33333333333333 0.66666666666667 0.25000000000000 Ti (2c) 0.66666666666667 0.33333333333333 0.75000000000000 Ti (2c)