A4B2C13D_tP40_90_g_d_cef2g_c & a,c/a,z1,z2,z3,x4,x5,x6,y6,z6,x7,y7,z7,x8,y8,z8 --params=7.3739946979,1.45226471387,-0.0654,0.7769,0.83072,0.6476,0.7846,0.648,0.751,0.001,0.7502,0.5354,0.32757,0.7289,0.8811,0.2635 & P42_{1}2 D_{4}^{2} #90 (c^2defg^3) & tP40 & None & Na4Ti2Si8O22[H2O]4 & & S. Ferdov et al., Acta Crystallogr. E 63, i186-i186 (2007) 1.00000000000000 7.37399469790000 0.00000000000000 0.00000000000000 0.00000000000000 7.37399469790000 0.00000000000000 0.00000000000000 0.00000000000000 10.70899230000000 H Na O Ti 8 4 26 2 Direct 0.64800000000000 0.75100000000000 0.00100000000000 H (8g) -0.64800000000000 -0.75100000000000 0.00100000000000 H (8g) -0.25100000000000 1.14800000000000 0.00100000000000 H (8g) 1.25100000000000 -0.14800000000000 0.00100000000000 H (8g) -0.14800000000000 1.25100000000000 -0.00100000000000 H (8g) 1.14800000000000 -0.25100000000000 -0.00100000000000 H (8g) 0.75100000000000 0.64800000000000 -0.00100000000000 H (8g) -0.75100000000000 -0.64800000000000 -0.00100000000000 H (8g) 0.00000000000000 0.00000000000000 0.83072000000000 Na (4d) 0.50000000000000 0.50000000000000 0.83072000000000 Na (4d) 0.50000000000000 0.50000000000000 -0.83072000000000 Na (4d) 0.00000000000000 0.00000000000000 -0.83072000000000 Na (4d) 0.00000000000000 0.50000000000000 -0.06540000000000 O (2c) 0.50000000000000 0.00000000000000 0.06540000000000 O (2c) 0.64760000000000 0.64760000000000 0.00000000000000 O (4e) -0.64760000000000 -0.64760000000000 0.00000000000000 O (4e) -0.14760000000000 1.14760000000000 0.00000000000000 O (4e) 1.14760000000000 -0.14760000000000 0.00000000000000 O (4e) 0.78460000000000 0.78460000000000 0.50000000000000 O (4f) -0.78460000000000 -0.78460000000000 0.50000000000000 O (4f) -0.28460000000000 1.28460000000000 0.50000000000000 O (4f) 1.28460000000000 -0.28460000000000 0.50000000000000 O (4f) 0.75020000000000 0.53540000000000 0.32757000000000 O (8g) -0.75020000000000 -0.53540000000000 0.32757000000000 O (8g) -0.03540000000000 1.25020000000000 0.32757000000000 O (8g) 1.03540000000000 -0.25020000000000 0.32757000000000 O (8g) -0.25020000000000 1.03540000000000 -0.32757000000000 O (8g) 1.25020000000000 -0.03540000000000 -0.32757000000000 O (8g) 0.53540000000000 0.75020000000000 -0.32757000000000 O (8g) -0.53540000000000 -0.75020000000000 -0.32757000000000 O (8g) 0.72890000000000 0.88110000000000 0.26350000000000 O (8g) -0.72890000000000 -0.88110000000000 0.26350000000000 O (8g) -0.38110000000000 1.22890000000000 0.26350000000000 O (8g) 1.38110000000000 -0.22890000000000 0.26350000000000 O (8g) -0.22890000000000 1.38110000000000 -0.26350000000000 O (8g) 1.22890000000000 -0.38110000000000 -0.26350000000000 O (8g) 0.88110000000000 0.72890000000000 -0.26350000000000 O (8g) -0.88110000000000 -0.72890000000000 -0.26350000000000 O (8g) 0.00000000000000 0.50000000000000 0.77690000000000 Ti (2c) 0.50000000000000 0.00000000000000 -0.77690000000000 Ti (2c)