A4B9_cP52_215_ei_3efgi & a,x1,x2,x3,x4,x5,x6,x7,z7,x8,z8 --params=8.7068,0.1157,0.8296,0.3253,0.6066,0.3534,0.8549,0.8113,0.5332,0.3153,0.0322 & P-43m T_{d}^{1} #215 (e^4fgi^2) & cP52 & $D8_{3}$ & Cu9Al4 & $\gamma$-brass Cu$_{9}$Al$_{4}$ & L. Arnberg and S. Westman, Acta Crystallogr. Sect. A 34, 399-404 (1978) 1.00000000000000 8.70680000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.70680000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.70680000000000 Al Cu 16 36 Direct 0.11570000000000 0.11570000000000 0.11570000000000 Al (4e) -0.11570000000000 -0.11570000000000 0.11570000000000 Al (4e) -0.11570000000000 0.11570000000000 -0.11570000000000 Al (4e) 0.11570000000000 -0.11570000000000 -0.11570000000000 Al (4e) 0.81130000000000 0.81130000000000 0.53320000000000 Al (12i) -0.81130000000000 -0.81130000000000 0.53320000000000 Al (12i) -0.81130000000000 0.81130000000000 -0.53320000000000 Al (12i) 0.81130000000000 -0.81130000000000 -0.53320000000000 Al (12i) 0.53320000000000 0.81130000000000 0.81130000000000 Al (12i) 0.53320000000000 -0.81130000000000 -0.81130000000000 Al (12i) -0.53320000000000 -0.81130000000000 0.81130000000000 Al (12i) -0.53320000000000 0.81130000000000 -0.81130000000000 Al (12i) 0.81130000000000 0.53320000000000 0.81130000000000 Al (12i) -0.81130000000000 0.53320000000000 -0.81130000000000 Al (12i) 0.81130000000000 -0.53320000000000 -0.81130000000000 Al (12i) -0.81130000000000 -0.53320000000000 0.81130000000000 Al (12i) 0.82960000000000 0.82960000000000 0.82960000000000 Cu (4e) -0.82960000000000 -0.82960000000000 0.82960000000000 Cu (4e) -0.82960000000000 0.82960000000000 -0.82960000000000 Cu (4e) 0.82960000000000 -0.82960000000000 -0.82960000000000 Cu (4e) 0.32530000000000 0.32530000000000 0.32530000000000 Cu (4e) -0.32530000000000 -0.32530000000000 0.32530000000000 Cu (4e) -0.32530000000000 0.32530000000000 -0.32530000000000 Cu (4e) 0.32530000000000 -0.32530000000000 -0.32530000000000 Cu (4e) 0.60660000000000 0.60660000000000 0.60660000000000 Cu (4e) -0.60660000000000 -0.60660000000000 0.60660000000000 Cu (4e) -0.60660000000000 0.60660000000000 -0.60660000000000 Cu (4e) 0.60660000000000 -0.60660000000000 -0.60660000000000 Cu (4e) 0.35340000000000 0.00000000000000 0.00000000000000 Cu (6f) -0.35340000000000 0.00000000000000 0.00000000000000 Cu (6f) 0.00000000000000 0.35340000000000 0.00000000000000 Cu (6f) 0.00000000000000 -0.35340000000000 0.00000000000000 Cu (6f) 0.00000000000000 0.00000000000000 0.35340000000000 Cu (6f) 0.00000000000000 0.00000000000000 -0.35340000000000 Cu (6f) 0.85490000000000 0.50000000000000 0.50000000000000 Cu (6g) -0.85490000000000 0.50000000000000 0.50000000000000 Cu (6g) 0.50000000000000 0.85490000000000 0.50000000000000 Cu (6g) 0.50000000000000 -0.85490000000000 0.50000000000000 Cu (6g) 0.50000000000000 0.50000000000000 0.85490000000000 Cu (6g) 0.50000000000000 0.50000000000000 -0.85490000000000 Cu (6g) 0.31530000000000 0.31530000000000 0.03220000000000 Cu (12i) -0.31530000000000 -0.31530000000000 0.03220000000000 Cu (12i) -0.31530000000000 0.31530000000000 -0.03220000000000 Cu (12i) 0.31530000000000 -0.31530000000000 -0.03220000000000 Cu (12i) 0.03220000000000 0.31530000000000 0.31530000000000 Cu (12i) 0.03220000000000 -0.31530000000000 -0.31530000000000 Cu (12i) -0.03220000000000 -0.31530000000000 0.31530000000000 Cu (12i) -0.03220000000000 0.31530000000000 -0.31530000000000 Cu (12i) 0.31530000000000 0.03220000000000 0.31530000000000 Cu (12i) -0.31530000000000 0.03220000000000 -0.31530000000000 Cu (12i) 0.31530000000000 -0.03220000000000 -0.31530000000000 Cu (12i) -0.31530000000000 -0.03220000000000 0.31530000000000 Cu (12i)