A4BC4D_tI40_122_e_b_e_a & a,c/a,x3,y3,z3,x4,y4,z4 --params=7.4264,0.933292039211,0.14867,0.22713,0.12266,0.1933,0.08283,0.12675 & I-42d D_{2d}^{12} #122 (abe^2) & tI40 & $H2_{2}$ & KH2PO4 & KH2PO4 & R. J. Nelmes and G. M. Meyer and J. E. Tibballs, J. Phys. C: Solid State Phys. 15, 59-75 (1982) 1.00000000000000 -3.71320000000000 3.71320000000000 3.46550000000000 3.71320000000000 -3.71320000000000 3.46550000000000 3.71320000000000 3.71320000000000 -3.46550000000000 H K O P 8 2 8 2 Direct 0.34979000000000 0.27133000000000 0.37580000000000 H (16e) -0.10447000000000 -0.02601000000000 -0.37580000000000 H (16e) -0.27133000000000 0.10447000000000 0.07846000000000 H (16e) 0.02601000000000 -0.34979000000000 -0.07846000000000 H (16e) 0.85447000000000 -0.02133000000000 0.57846000000000 H (16e) 0.40021000000000 0.27601000000000 0.42154000000000 H (16e) 0.72399000000000 0.14553000000000 0.12420000000000 H (16e) 1.02133000000000 0.59979000000000 0.87580000000000 H (16e) 0.50000000000000 0.50000000000000 0.00000000000000 K (4b) 0.25000000000000 0.75000000000000 0.50000000000000 K (4b) 0.20958000000000 0.32005000000000 0.27613000000000 O (16e) 0.04392000000000 -0.06655000000000 -0.27613000000000 O (16e) -0.32005000000000 -0.04392000000000 -0.11047000000000 O (16e) 0.06655000000000 -0.20958000000000 0.11047000000000 O (16e) 0.70608000000000 -0.07005000000000 0.38953000000000 O (16e) 0.54042000000000 0.31655000000000 0.61047000000000 O (16e) 0.68345000000000 0.29392000000000 0.22387000000000 O (16e) 1.07005000000000 0.45958000000000 0.77613000000000 O (16e) 0.00000000000000 0.00000000000000 0.00000000000000 P (4a) 0.75000000000000 0.25000000000000 0.50000000000000 P (4a)