A5BC2_mC64_15_5f_f_2f & a,b/a,c/a,beta,x1,y1,z1,x2,y2,z2,x3,y3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6,x7,y7,z7,x8,y8,z8 --params=14.43,0.466597366597,0.721413721414,122.13,0.089,0.002,0.143,0.118,0.287,0.318,0.297,0.429,0.06,0.298,0.157,0.33,0.485,0.102,0.103,0.181,0.093,0.308,0.037,0.257,0.466,0.359,0.122,0.165 & C2/c C_{2h}^{6} #15 (f^8) & mC64 & None & O5SiY2 & O5SiY2 & G. V. Anan'eva et al., Inorg. Mat. 17, 754-758 (1981) 1.00000000000000 7.21500000000000 -3.36650000000000 0.00000000000000 7.21500000000000 3.36650000000000 0.00000000000000 -5.53647583060549 0.00000000000000 8.81564151818353 O Si Y 20 4 8 Direct 0.08700000000000 0.09100000000000 0.14300000000000 O (8f) -0.09100000000000 -0.08700000000000 0.35700000000000 O (8f) -0.08700000000000 -0.09100000000000 -0.14300000000000 O (8f) 0.09100000000000 0.08700000000000 0.64300000000000 O (8f) -0.16900000000000 0.40500000000000 0.31800000000000 O (8f) -0.40500000000000 0.16900000000000 0.18200000000000 O (8f) 0.16900000000000 -0.40500000000000 -0.31800000000000 O (8f) 0.40500000000000 -0.16900000000000 0.81800000000000 O (8f) -0.13200000000000 0.72600000000000 0.06000000000000 O (8f) -0.72600000000000 0.13200000000000 0.44000000000000 O (8f) 0.13200000000000 -0.72600000000000 -0.06000000000000 O (8f) 0.72600000000000 -0.13200000000000 0.56000000000000 O (8f) 0.14100000000000 0.45500000000000 0.33000000000000 O (8f) -0.45500000000000 -0.14100000000000 0.17000000000000 O (8f) -0.14100000000000 -0.45500000000000 -0.33000000000000 O (8f) 0.45500000000000 0.14100000000000 0.83000000000000 O (8f) 0.38300000000000 0.58700000000000 0.10300000000000 O (8f) -0.58700000000000 -0.38300000000000 0.39700000000000 O (8f) -0.38300000000000 -0.58700000000000 -0.10300000000000 O (8f) 0.58700000000000 0.38300000000000 0.60300000000000 O (8f) 0.08800000000000 0.27400000000000 0.30800000000000 Si (8f) -0.27400000000000 -0.08800000000000 0.19200000000000 Si (8f) -0.08800000000000 -0.27400000000000 -0.30800000000000 Si (8f) 0.27400000000000 0.08800000000000 0.80800000000000 Si (8f) -0.22000000000000 0.29400000000000 0.46600000000000 Y (8f) -0.29400000000000 0.22000000000000 0.03400000000000 Y (8f) 0.22000000000000 -0.29400000000000 -0.46600000000000 Y (8f) 0.29400000000000 -0.22000000000000 0.96600000000000 Y (8f) 0.23700000000000 0.48100000000000 0.16500000000000 Y (8f) -0.48100000000000 -0.23700000000000 0.33500000000000 Y (8f) -0.23700000000000 -0.48100000000000 -0.16500000000000 Y (8f) 0.48100000000000 0.23700000000000 0.66500000000000 Y (8f)