A8B5_hR26_160_a3bc_a3b & a,c/a,x1,x2,x3,z3,x4,z4,x5,z5,x6,z6,x7,z7,x8,z8,x9,y9,z9 --params=12.71838,0.624030733474,0.672,0.194,0.654,0.01201,0.349,0.58199,0.722,0.35601,1.003,-0.20599,0.998,-0.66,0.355,1.00601,1.033,-0.339,0.28799 & R3m C_{3v}^{5} #160 (a^2b^6c) & hR26 & $D8_{10}$ & Cr5Al8 & & A. J. Bradley and S. S. Lu, Zeitschrift f\"{u}r Kristallographie - Crystalline Materials 96, 20-37 (1937) 1.00000000000000 6.35919000000000 -3.67148005832798 2.64555333333333 0.00000000000000 7.34296011665595 2.64555333333333 -6.35919000000000 -3.67148005832798 2.64555333333333 Al Cr 16 10 Direct 0.67200000000000 0.67200000000000 0.67200000000000 Al (1a) 0.65400000000000 0.65400000000000 0.01201000000000 Al (3b) 0.01201000000000 0.65400000000000 0.65400000000000 Al (3b) 0.65400000000000 0.01201000000000 0.65400000000000 Al (3b) 0.34900000000000 0.34900000000000 0.58199000000000 Al (3b) 0.58199000000000 0.34900000000000 0.34900000000000 Al (3b) 0.34900000000000 0.58199000000000 0.34900000000000 Al (3b) 0.72200000000000 0.72200000000000 0.35601000000000 Al (3b) 0.35601000000000 0.72200000000000 0.72200000000000 Al (3b) 0.72200000000000 0.35601000000000 0.72200000000000 Al (3b) 1.03300000000000 -0.33900000000000 0.28799000000000 Al (6c) 0.28799000000000 1.03300000000000 -0.33900000000000 Al (6c) -0.33900000000000 0.28799000000000 1.03300000000000 Al (6c) 0.28799000000000 -0.33900000000000 1.03300000000000 Al (6c) -0.33900000000000 1.03300000000000 0.28799000000000 Al (6c) 1.03300000000000 0.28799000000000 -0.33900000000000 Al (6c) 0.19400000000000 0.19400000000000 0.19400000000000 Cr (1a) 1.00300000000000 1.00300000000000 -0.20599000000000 Cr (3b) -0.20599000000000 1.00300000000000 1.00300000000000 Cr (3b) 1.00300000000000 -0.20599000000000 1.00300000000000 Cr (3b) 0.99800000000000 0.99800000000000 -0.66000000000000 Cr (3b) -0.66000000000000 0.99800000000000 0.99800000000000 Cr (3b) 0.99800000000000 -0.66000000000000 0.99800000000000 Cr (3b) 0.35500000000000 0.35500000000000 1.00601000000000 Cr (3b) 1.00601000000000 0.35500000000000 0.35500000000000 Cr (3b) 0.35500000000000 1.00601000000000 0.35500000000000 Cr (3b)