A9B2C9_hP40_176_hi_f_hi & a,c/a,z1,x2,y2,x3,y3,x4,y4,z4,x5,y5,z5 --params=6.436,2.50512740833,0.17175,0.332,0.9098,0.331,0.0895,0.338,0.4243,0.1133,0.3441,0.2817,0.0747 & P6_{3}/m C_{6h}^{2} #176 (fh^2i^2) & hP40 & $F4_{1}$ & C9Fe2O9 & C9Fe2O9 & F. A. Cotton and J. M. Troup, {J. Chem. Soc. Dalton Trans. , 800-802 (1974) 1.00000000000000 3.21800000000000 -5.57373949875665 0.00000000000000 3.21800000000000 5.57373949875665 0.00000000000000 0.00000000000000 0.00000000000000 16.12300000000000 C Fe O 18 4 18 Direct 0.33200000000000 0.90980000000000 0.25000000000000 C (6h) -0.90980000000000 -0.57780000000000 0.25000000000000 C (6h) 0.57780000000000 -0.33200000000000 0.25000000000000 C (6h) -0.33200000000000 -0.90980000000000 0.75000000000000 C (6h) 0.90980000000000 0.57780000000000 0.75000000000000 C (6h) -0.57780000000000 0.33200000000000 0.75000000000000 C (6h) 0.33800000000000 0.42430000000000 0.11330000000000 C (12i) -0.42430000000000 -0.08630000000000 0.11330000000000 C (12i) 0.08630000000000 -0.33800000000000 0.11330000000000 C (12i) -0.33800000000000 -0.42430000000000 0.61330000000000 C (12i) 0.42430000000000 0.08630000000000 0.61330000000000 C (12i) -0.08630000000000 0.33800000000000 0.61330000000000 C (12i) -0.33800000000000 -0.42430000000000 -0.11330000000000 C (12i) 0.42430000000000 0.08630000000000 -0.11330000000000 C (12i) -0.08630000000000 0.33800000000000 -0.11330000000000 C (12i) 0.33800000000000 0.42430000000000 0.38670000000000 C (12i) -0.42430000000000 -0.08630000000000 0.38670000000000 C (12i) 0.08630000000000 -0.33800000000000 0.38670000000000 C (12i) 0.33333333333333 0.66666666666667 0.17175000000000 Fe (4f) 0.66666666666667 0.33333333333333 0.67175000000000 Fe (4f) 0.66666666666667 0.33333333333333 -0.17175000000000 Fe (4f) 0.33333333333333 0.66666666666667 0.32825000000000 Fe (4f) 0.33100000000000 0.08950000000000 0.25000000000000 O (6h) -0.08950000000000 0.24150000000000 0.25000000000000 O (6h) -0.24150000000000 -0.33100000000000 0.25000000000000 O (6h) -0.33100000000000 -0.08950000000000 0.75000000000000 O (6h) 0.08950000000000 -0.24150000000000 0.75000000000000 O (6h) 0.24150000000000 0.33100000000000 0.75000000000000 O (6h) 0.34410000000000 0.28170000000000 0.07470000000000 O (12i) -0.28170000000000 0.06240000000000 0.07470000000000 O (12i) -0.06240000000000 -0.34410000000000 0.07470000000000 O (12i) -0.34410000000000 -0.28170000000000 0.57470000000000 O (12i) 0.28170000000000 -0.06240000000000 0.57470000000000 O (12i) 0.06240000000000 0.34410000000000 0.57470000000000 O (12i) -0.34410000000000 -0.28170000000000 -0.07470000000000 O (12i) 0.28170000000000 -0.06240000000000 -0.07470000000000 O (12i) 0.06240000000000 0.34410000000000 -0.07470000000000 O (12i) 0.34410000000000 0.28170000000000 0.42530000000000 O (12i) -0.28170000000000 0.06240000000000 0.42530000000000 O (12i) -0.06240000000000 -0.34410000000000 0.42530000000000 O (12i)