AB2C3D2_tP32_127_g_eh_gk_k & a,c/a,z1,x2,x3,x4,x5,z5,x6,z6 --params=8.16,1.08860294118,0.7572,0.3257,0.211,0.3521,0.3726,0.1269,0.1659,0.2594 & P4/mbm D_{4h}^{5} #127 (eg^2hk^2) & tP32 & None & CCl2O3Pb2 & Phosgenite & G. Giuseppetti and C. Tadini, Tschermaks Min. Petr. Mitt. 21, 101-109 (1974) 1.00000000000000 8.16000000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.16000000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.88300000000000 C Cl O Pb 4 8 12 8 Direct 0.32570000000000 0.82570000000000 0.00000000000000 C (4g) -0.32570000000000 0.17430000000000 0.00000000000000 C (4g) 0.17430000000000 0.32570000000000 0.00000000000000 C (4g) 0.82570000000000 -0.32570000000000 0.00000000000000 C (4g) 0.00000000000000 0.00000000000000 0.75720000000000 Cl (4e) 0.50000000000000 0.50000000000000 -0.75720000000000 Cl (4e) 0.00000000000000 0.00000000000000 -0.75720000000000 Cl (4e) 0.50000000000000 0.50000000000000 0.75720000000000 Cl (4e) 0.35210000000000 0.85210000000000 0.50000000000000 Cl (4h) -0.35210000000000 0.14790000000000 0.50000000000000 Cl (4h) 0.14790000000000 0.35210000000000 0.50000000000000 Cl (4h) 0.85210000000000 -0.35210000000000 0.50000000000000 Cl (4h) 0.21100000000000 0.71100000000000 0.00000000000000 O (4g) -0.21100000000000 0.28900000000000 0.00000000000000 O (4g) 0.28900000000000 0.21100000000000 0.00000000000000 O (4g) 0.71100000000000 -0.21100000000000 0.00000000000000 O (4g) 0.37260000000000 0.87260000000000 0.12690000000000 O (8k) -0.37260000000000 0.12740000000000 0.12690000000000 O (8k) 0.12740000000000 0.37260000000000 0.12690000000000 O (8k) 0.87260000000000 -0.37260000000000 0.12690000000000 O (8k) 0.12740000000000 0.37260000000000 -0.12690000000000 O (8k) 0.87260000000000 -0.37260000000000 -0.12690000000000 O (8k) 0.37260000000000 0.87260000000000 -0.12690000000000 O (8k) -0.37260000000000 0.12740000000000 -0.12690000000000 O (8k) 0.16590000000000 0.66590000000000 0.25940000000000 Pb (8k) -0.16590000000000 0.33410000000000 0.25940000000000 Pb (8k) 0.33410000000000 0.16590000000000 0.25940000000000 Pb (8k) 0.66590000000000 -0.16590000000000 0.25940000000000 Pb (8k) 0.33410000000000 0.16590000000000 -0.25940000000000 Pb (8k) 0.66590000000000 -0.16590000000000 -0.25940000000000 Pb (8k) 0.16590000000000 0.66590000000000 -0.25940000000000 Pb (8k) -0.16590000000000 0.33410000000000 -0.25940000000000 Pb (8k)