AB2_oF48_70_g_fg & a,b/a,c/a,y1,z2,z3 --params=5.275,1.71450236967,3.47450236967,0.4586,0.49819,0.0415 & Fddd D_{2h}^{24} #70 (fg^2) & oF48 & $C_{b}$ & CuMg2 & CuMg2 & F. Gingl and P. Selvam and K. Yvon, Acta Crystallogr. Sect. B Struct. Sci. 49, 201-203 (1993) 1.00000000000000 0.00000000000000 4.52200000000000 9.16400000000000 2.63750000000000 0.00000000000000 9.16400000000000 2.63750000000000 4.52200000000000 0.00000000000000 Cu Mg 4 8 Direct 0.49819000000000 0.49819000000000 -0.24819000000000 Cu (16g) -0.24819000000000 -0.24819000000000 0.49819000000000 Cu (16g) -0.49819000000000 -0.49819000000000 1.24819000000000 Cu (16g) 1.24819000000000 1.24819000000000 -0.49819000000000 Cu (16g) 0.45860000000000 -0.20860000000000 0.45860000000000 Mg (16f) -0.20860000000000 0.45860000000000 -0.20860000000000 Mg (16f) -0.45860000000000 1.20860000000000 -0.45860000000000 Mg (16f) 1.20860000000000 -0.45860000000000 1.20860000000000 Mg (16f) 0.04150000000000 0.04150000000000 0.20850000000000 Mg (16g) 0.20850000000000 0.20850000000000 0.04150000000000 Mg (16g) -0.04150000000000 -0.04150000000000 0.79150000000000 Mg (16g) 0.79150000000000 0.79150000000000 -0.04150000000000 Mg (16g)