AB2_tI48_122_cd_2e & a,c/a,z1,x2,x3,y3,z3,x4,y4,z4 --params=9.5965,1.22841661022,0.16953,0.27647,0.03373,0.24952,0.29644,0.14693,0.116,0.39956 & I-42d D_{2d}^{12} #122 (cde^2) & tI48 & None & NaS2 & NaS2 & R. Tegman, Acta Crystallogr. Sect. B Struct. Sci. 29, 1463-1469 (1973) 1.00000000000000 -4.79825000000000 4.79825000000000 5.89425000000000 4.79825000000000 -4.79825000000000 5.89425000000000 4.79825000000000 4.79825000000000 -5.89425000000000 Na S 8 16 Direct 0.16953000000000 0.16953000000000 0.00000000000000 Na (8c) -0.16953000000000 -0.16953000000000 0.00000000000000 Na (8c) 0.58047000000000 0.08047000000000 0.50000000000000 Na (8c) 0.91953000000000 0.41953000000000 0.50000000000000 Na (8c) 0.37500000000000 0.40147000000000 0.52647000000000 Na (8d) 0.87500000000000 -0.15147000000000 0.47353000000000 Na (8d) 0.59853000000000 0.12500000000000 -0.02647000000000 Na (8d) 1.15147000000000 0.62500000000000 1.02647000000000 Na (8d) 0.54596000000000 0.33017000000000 0.28325000000000 S (16e) 0.04692000000000 0.26271000000000 -0.28325000000000 S (16e) -0.33017000000000 -0.04692000000000 0.21579000000000 S (16e) -0.26271000000000 -0.54596000000000 -0.21579000000000 S (16e) 0.70308000000000 -0.08017000000000 0.71579000000000 S (16e) 0.20404000000000 -0.01271000000000 0.28421000000000 S (16e) 1.01271000000000 0.29692000000000 0.21675000000000 S (16e) 1.08017000000000 0.79596000000000 0.78325000000000 S (16e) 0.51556000000000 0.54649000000000 0.26293000000000 S (16e) 0.28356000000000 0.25263000000000 -0.26293000000000 S (16e) -0.54649000000000 -0.28356000000000 -0.03093000000000 S (16e) -0.25263000000000 -0.51556000000000 0.03093000000000 S (16e) 0.46644000000000 -0.29649000000000 0.46907000000000 S (16e) 0.23444000000000 -0.00263000000000 0.53093000000000 S (16e) 1.00263000000000 0.53356000000000 0.23707000000000 S (16e) 1.29649000000000 0.76556000000000 0.76293000000000 S (16e)