AB3_oP16_62_c_cd & a,b/a,c/a,x1,z1,x2,z2,x3,y3,z3 --params=5.09,1.3257367387,0.888605108055,0.39,0.05,0.036,0.852,0.186,0.063,0.328 & Pnma D^{16}_{2h} #62 (c^2d) & oP16 & D0_11 & Fe3C & Cementite & F. H. Herbstein and J. Smuts, Acta Cryst. 17, 1331-1332 (1964) 1.0000000000000000 5.09000000000000 0.00000000000000 0.00000000000000 0.00000000000000 6.74800000000000 0.00000000000000 0.00000000000000 0.00000000000000 4.52300000000000 C Fe 4 12 Direct 0.11000000000000 0.75000000000000 -0.45000000000000 C (4c) 0.39000000000000 0.25000000000000 0.05000000000000 C (4c) 0.61000000000000 0.75000000000000 0.95000000000000 C (4c) 0.89000000000000 0.25000000000000 0.45000000000000 C (4c) 0.03600000000000 0.25000000000000 0.85200000000000 Fe (4c) -0.03600000000000 0.75000000000000 0.14800000000000 Fe (4c) 0.46400000000000 0.75000000000000 0.35200000000000 Fe (4c) 0.53600000000000 0.25000000000000 0.64800000000000 Fe (4c) 0.18600000000000 0.06300000000000 0.32800000000000 Fe (8d) 0.18600000000000 0.43700000000000 0.32800000000000 Fe (8d) 0.31400000000000 -0.06300000000000 0.82800000000000 Fe (8d) 0.31400000000000 0.56300000000000 0.82800000000000 Fe (8d) 0.68600000000000 0.06300000000000 0.17200000000000 Fe (8d) 0.68600000000000 0.43700000000000 0.17200000000000 Fe (8d) 0.81400000000000 0.56300000000000 0.67200000000000 Fe (8d) 0.81400000000000 0.93700000000000 0.67200000000000 Fe (8d)