AB3_tP32_86_g_3g & a,c/a,x1,y1,z1,x2,y2,z2,x3,y3,z3,x4,y4,z4 --params=9.997999333,0.499899979999,0.0439,0.20812,0.5354,0.11009,0.22151,0.0295,0.14275,0.66613,0.7153,0.53342,0.06957,0.7593 & P4_{2}/n C_{4h}^{4} #86 (g^4) & tP32 & None & Ti3P & & V. N. Eremenko and V. E. Listovnichii, (1965) 1.00000000000000 9.99799933300000 0.00000000000000 0.00000000000000 0.00000000000000 9.99799933300000 0.00000000000000 0.00000000000000 0.00000000000000 4.99799966660000 P Ti 8 24 Direct 0.04390000000000 0.20812000000000 0.53540000000000 P (8g) 0.45610000000000 0.29188000000000 0.53540000000000 P (8g) -0.20812000000000 0.54390000000000 1.03540000000000 P (8g) 0.70812000000000 -0.04390000000000 1.03540000000000 P (8g) -0.04390000000000 -0.20812000000000 -0.53540000000000 P (8g) 0.54390000000000 0.70812000000000 -0.53540000000000 P (8g) 0.20812000000000 0.45610000000000 -0.03540000000000 P (8g) 0.29188000000000 0.04390000000000 -0.03540000000000 P (8g) 0.11009000000000 0.22151000000000 0.02950000000000 Ti (8g) 0.38991000000000 0.27849000000000 0.02950000000000 Ti (8g) -0.22151000000000 0.61009000000000 0.52950000000000 Ti (8g) 0.72151000000000 -0.11009000000000 0.52950000000000 Ti (8g) -0.11009000000000 -0.22151000000000 -0.02950000000000 Ti (8g) 0.61009000000000 0.72151000000000 -0.02950000000000 Ti (8g) 0.22151000000000 0.38991000000000 0.47050000000000 Ti (8g) 0.27849000000000 0.11009000000000 0.47050000000000 Ti (8g) 0.14275000000000 0.66613000000000 0.71530000000000 Ti (8g) 0.35725000000000 -0.16613000000000 0.71530000000000 Ti (8g) -0.66613000000000 0.64275000000000 1.21530000000000 Ti (8g) 1.16613000000000 -0.14275000000000 1.21530000000000 Ti (8g) -0.14275000000000 -0.66613000000000 -0.71530000000000 Ti (8g) 0.64275000000000 1.16613000000000 -0.71530000000000 Ti (8g) 0.66613000000000 0.35725000000000 -0.21530000000000 Ti (8g) -0.16613000000000 0.14275000000000 -0.21530000000000 Ti (8g) 0.53342000000000 0.06957000000000 0.75930000000000 Ti (8g) -0.03342000000000 0.43043000000000 0.75930000000000 Ti (8g) -0.06957000000000 1.03342000000000 1.25930000000000 Ti (8g) 0.56957000000000 -0.53342000000000 1.25930000000000 Ti (8g) -0.53342000000000 -0.06957000000000 -0.75930000000000 Ti (8g) 1.03342000000000 0.56957000000000 -0.75930000000000 Ti (8g) 0.06957000000000 -0.03342000000000 -0.25930000000000 Ti (8g) 0.43043000000000 0.53342000000000 -0.25930000000000 Ti (8g)