ABC2_mC16_15_e_e_f & a,b/a,c/a,beta,y1,y2,x3,y3,z3 --params=7.084,1.595567476,0.761434217956,113.2,-0.00332,0.3572,0.196,0.1098,0.1068 & C2/c C_{2h}^{6} #15 (e^2f) & mC16 & $F5_{a}$ & FeKS2 & FeKS2 & W. Bronger and A. Kyas and P. M\"{u}ller, J. Solid State Chem. 70, 262-270 (1987) 1.00000000000000 3.54200000000000 -5.65150000000000 0.00000000000000 3.54200000000000 5.65150000000000 0.00000000000000 -2.12492266033359 0.00000000000000 4.95781601994273 Fe K S 2 2 4 Direct 0.00332000000000 -0.00332000000000 0.25000000000000 Fe (4e) -0.00332000000000 0.00332000000000 0.75000000000000 Fe (4e) -0.35720000000000 0.35720000000000 0.25000000000000 K (4e) 0.35720000000000 -0.35720000000000 0.75000000000000 K (4e) 0.08620000000000 0.30580000000000 0.10680000000000 S (8f) -0.30580000000000 -0.08620000000000 0.39320000000000 S (8f) -0.08620000000000 -0.30580000000000 -0.10680000000000 S (8f) 0.30580000000000 0.08620000000000 0.60680000000000 S (8f)