AB_hR26_148_b2f_a2f & a,c/a,x3,y3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6 --params=15.659,0.335334312536,0.054,0.346,0.098,0.754,0.15699,0.6,0.555,0.84401,0.599,0.252,0.65501,0.098 & R(-3) C_{3i}^2 #148 (abf^4) & hR26 & & PdAl & beta' & T. Matkovi\'{c} and K. Schubert, J. Less Common Metals 55, 45-52 (1977) 1.0000000000000000 7.82950000000000 -4.52036393262018 1.75033333333333 0.00000000000000 9.04072786524035 1.75033333333333 -7.82950000000000 -4.52036393262018 1.75033333333333 Al Pd 13 13 Direct 0.50000000000000 0.50000000000000 0.50000000000000 Al (1b) 0.05400000000000 0.34600000000000 0.09800000000000 Al (6f) -0.05400000000000 0.65400000000000 -0.09800000000000 Al (6f) 0.09800000000000 0.05400000000000 0.34600000000000 Al (6f) -0.09800000000000 -0.05400000000000 0.65400000000000 Al (6f) 0.34600000000000 0.09800000000000 0.05400000000000 Al (6f) 0.65400000000000 -0.09800000000000 -0.05400000000000 Al (6f) -0.15700000000000 0.40000000000000 0.24600000000000 Al (6f) 0.15700000000000 0.60000000000000 0.75400000000000 Al (6f) 0.24600000000000 -0.15700000000000 0.40000000000000 Al (6f) 0.40000000000000 0.24600000000000 -0.15700000000000 Al (6f) 0.60000000000000 0.75400000000000 0.15700000000000 Al (6f) 0.75400000000000 0.15700000000000 0.60000000000000 Al (6f) 0.00000000000000 0.00000000000000 0.00000000000000 Pd (1a) 0.15600000000000 0.40100000000000 0.44500000000000 Pd (6f) 0.40100000000000 0.44500000000000 0.15600000000000 Pd (6f) 0.44500000000000 0.15600000000000 0.40100000000000 Pd (6f) 0.55500000000000 0.84400000000000 0.59900000000000 Pd (6f) 0.59900000000000 0.55500000000000 0.84400000000000 Pd (6f) 0.84400000000000 0.59900000000000 0.55500000000000 Pd (6f) 0.09800000000000 0.25200000000000 0.65500000000000 Pd (6f) -0.09800000000000 0.74800000000000 0.34500000000000 Pd (6f) 0.25200000000000 0.65500000000000 0.09800000000000 Pd (6f) 0.34500000000000 -0.09800000000000 0.74800000000000 Pd (6f) 0.65500000000000 0.09800000000000 0.25200000000000 Pd (6f) 0.74800000000000 0.34500000000000 -0.09800000000000 Pd (6f)