sigma_tP30_136_bf2ij & a,c/a,x2,x3,y3,x4,y4,x5,z5 --params==8.7966,0.518177,0.10136,0.36878,0.03651,0.56609,0.23933,0.31733,0.25202 & P4_2/mnm D_{4h}^{14} #136 (bfi^2j) & tP30 & D8_b & CrFe & sigma (disordered) & H. L. Yakel, Acta Cryst B 39, 20-28 (1983) 1.000000 8.79660000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.79660000000000 0.00000000000000 0.00000000000000 0.00000000000000 4.55819579820000 M 30 Direct(30) [A30] 0.00000000000000 0.00000000000000 0.50000000000000 M (2b) 0.50000000000000 0.50000000000000 0.00000000000000 M (2b) 0.10136000000000 0.10136000000000 0.00000000000000 M (4f) 0.89864000000000 0.89864000000000 0.00000000000000 M (4f) 0.39864000000000 0.60136000000000 0.50000000000000 M (4f) 0.60136000000000 0.39864000000000 0.50000000000000 M (4f) 0.36878000000000 0.03651000000000 0.00000000000000 M (8i) 0.63122000000000 0.96349000000000 0.00000000000000 M (8i) 0.46349000000000 0.86878000000000 0.50000000000000 M (8i) 0.53651000000000 0.13122000000000 0.50000000000000 M (8i) 0.13122000000000 0.53651000000000 0.50000000000000 M (8i) 0.86878000000000 0.46349000000000 0.50000000000000 M (8i) 0.03651000000000 0.36878000000000 0.00000000000000 M (8i) 0.96349000000000 0.63122000000000 0.00000000000000 M (8i) 0.56609000000000 0.23933000000000 0.00000000000000 M (8i) 0.43391000000000 0.76067000000000 0.00000000000000 M (8i) 0.26067000000000 0.06609000000000 0.50000000000000 M (8i) 0.73933000000000 0.93391000000000 0.50000000000000 M (8i) 0.93391000000000 0.73933000000000 0.50000000000000 M (8i) 0.06609000000000 0.26067000000000 0.50000000000000 M (8i) 0.23933000000000 0.56609000000000 0.00000000000000 M (8i) 0.76067000000000 0.43391000000000 0.00000000000000 M (8i) 0.31733000000000 0.31733000000000 0.25202000000000 M (8j) 0.68267000000000 0.68267000000000 0.25202000000000 M (8j) 0.18267000000000 0.81733000000000 0.75202000000000 M (8j) 0.81733000000000 0.18267000000000 0.75202000000000 M (8j) 0.18267000000000 0.81733000000000 0.24798000000000 M (8j) 0.81733000000000 0.18267000000000 0.24798000000000 M (8j) 0.31733000000000 0.31733000000000 0.74798000000000 M (8j) 0.68267000000000 0.68267000000000 0.74798000000000 M (8j)