Encyclopedia of Crystallographic Prototypes

Tetragonal Space Groups (#75-#142)

  • M. J. Mehl, D. Hicks, C. Toher, O. Levy, R. M. Hanson, G. L. W. Hart, and S. Curtarolo, The AFLOW Library of Crystallographic Prototypes: Part 1, Comp. Mat. Sci. 136, S1-S828 (2017). (doi=10.1016/j.commatsci.2017.01.017)
  • D. Hicks, M. J. Mehl, E. Gossett, C. Toher, O. Levy, R. M. Hanson, G. L. W. Hart, and S. Curtarolo, The AFLOW Library of Crystallographic Prototypes: Part 2, Comp. Mat. Sci. 161, S1-S1011 (2019). (doi=10.1016/j.commatsci.2018.10.043)
  • D. Hicks, M.J. Mehl, M. Esters, C. Oses, O. Levy, G.L.W. Hart, C. Toher, and S. Curtarolo, The AFLOW Library of Crystallographic Prototypes: Part 3, Comp. Mat. Sci. 199, 110450 (2021). (doi=10.1016/j.commatsci.2021.110450)

$P4$ (#75)

$P4_{1}$ (#76)

$P4_{2}$ (#77)

$P4_{3}$ (#78)

$I4$ (#79)

$I4_{1}$ (#80)

$P\bar{4}$ (#81)

$I\bar{4}$ (#82)

$P4/m$ (#83)

$P4_{2}/m$ (#84)

$P4/n$ (#85)

$P4_{2}/n$ (#86)

$I4/m$ (#87)

$I4_{1}/a$ (#88)

$P422$ (#89)

$P42_{1}2$ (#90)

$P4_{1}22$ (#91)

$P4_{1}2_{1}2$ (#92)

$P4_{2}22$ (#93)

$P4_{2}2_{1}2$ (#94)

$P4_{3}22$ (#95)

$P4_{3}2_{1}2$ (#96)

$I422$ (#97)

$I4_{1}22$ (#98)

$P4mm$ (#99)

$P4bm$ (#100)

$P4_{2}cm$ (#101)

$P4_{2}nm$ (#102)

$P4cc$ (#103)

$P4nc$ (#104)

$P4_{2}mc$ (#105)

$P4_{2}bc$ (#106)

$I4mm$ (#107)

$I4cm$ (#108)

$I4_{1}md$ (#109)

$I4_{1}cd$ (#110)

$P\bar{4}2m$ (#111)

$P\bar{4}2c$ (#112)

$P\bar{4}2_{1}m$ (#113)

$P\bar{4}2_{1}c$ (#114)

$P\bar{4}m2$ (#115)

$P\bar{4}c2$ (#116)

$P\bar{4}b2$ (#117)

$P\bar{4}n2$ (#118)

$I\bar{4}m2$ (#119)

$I\bar{4}c2$ (#120)

$I\bar{4}2m$ (#121)

$I\bar{4}2d$ (#122)

$P4/mmm$ (#123)

$P4/mcc$ (#124)

$P4/nbm$ (#125)

$P4/nnc$ (#126)

$P4/mbm$ (#127)

$P4/mnc$ (#128)

$P4/nmm$ (#129)

$P4/ncc$ (#130)

$P4_{2}/mmc$ (#131)

$P4_{2}/mcm$ (#132)

$P4_{2}/nbc$ (#133)

$P4_{2}/nnm$ (#134)

$P4_{2}/mbc$ (#135)

$P4_{2}/mnm$ (#136)

$P4_{2}/nmc$ (#137)

$P4_{2}/ncm$ (#138)

$I4/mmm$ (#139)

$I4/mcm$ (#140)

$I4_{1}/amd$ (#141)

$I4_{1}/acd$ (#142)