A2B5CD2_oI40_44_2c_abcde_d_e & a,b/a,c/a,z1,z2,x3,z3,x4,z4,x5,z5,y6,z6,y7,z7,x8,y8,z8,x9,y9,z9 --params=8.367,1.28241902713,0.611330225887,0.5912,0.0195,0.374,0.19,0.4256,0.643,0.305,0.041,0.1669,0.1938,0.1465,0.5076,0.1602,0.2055,0.6362,0.2047,0.1613,0.0 & Imm2 C_{2v}^{20} #44 (abc^3d^2e^2) & oI40 & $S2_{2}$ & H2O5SiZn2 & Hemimorphite & R. J. Hill et al., Zeitschrift f{"u}r Kristallographie - Crystalline Materials 146, 241-259 (1977) 1.00000000000000 -4.18350000000000 5.36500000000000 2.55750000000000 4.18350000000000 -5.36500000000000 2.55750000000000 4.18350000000000 5.36500000000000 -2.55750000000000 H O Si Zn 4 10 2 4 Direct 0.19000000000000 0.56400000000000 0.37400000000000 H (4c) 0.19000000000000 -0.18400000000000 -0.37400000000000 H (4c) 0.64300000000000 1.06860000000000 0.42560000000000 H (4c) 0.64300000000000 0.21740000000000 -0.42560000000000 H (4c) 0.59120000000000 0.59120000000000 0.00000000000000 O (2a) 0.51950000000000 0.01950000000000 0.50000000000000 O (2b) 0.04100000000000 0.34600000000000 0.30500000000000 O (4c) 0.04100000000000 -0.26400000000000 -0.30500000000000 O (4c) 0.36070000000000 0.19380000000000 0.16690000000000 O (4d) 0.02690000000000 0.19380000000000 -0.16690000000000 O (4d) 0.84170000000000 0.79640000000000 0.36570000000000 O (8e) 0.43070000000000 0.47600000000000 -0.36570000000000 O (8e) 0.43070000000000 0.79640000000000 -0.04530000000000 O (8e) 0.84170000000000 0.47600000000000 0.04530000000000 O (8e) 0.65410000000000 0.50760000000000 0.14650000000000 Si (4d) 0.36110000000000 0.50760000000000 -0.14650000000000 Si (4d) 0.16130000000000 0.20470000000000 0.36600000000000 Zn (8e) -0.16130000000000 -0.20470000000000 -0.36600000000000 Zn (8e) -0.16130000000000 0.20470000000000 0.04340000000000 Zn (8e) 0.16130000000000 -0.20470000000000 -0.04340000000000 Zn (8e)