A2B_oP12_62_2c_c & a,b/a,c/a,x1,z1,x2,z2,x3,z3 --params=11.42,0.376532399299,0.805604203152,0.103,0.119,0.614,0.842,0.811,0.108 & Pnma D_{2h}^{16} #62 (c^3) & oP12 & $C53$ & Br2Sr & Br2Sr & M. A. Kamermans, Zeitschrift f{"u}r Kristallographie - Crystalline Materials 101, 406-411 (1939) 1.00000000000000 11.42000000000000 0.00000000000000 0.00000000000000 0.00000000000000 4.30000000000000 0.00000000000000 0.00000000000000 0.00000000000000 9.20000000000000 Br Sr 8 4 Direct 0.10300000000000 0.25000000000000 0.11900000000000 Br (4c) 0.39700000000000 0.75000000000000 0.61900000000000 Br (4c) -0.10300000000000 0.75000000000000 -0.11900000000000 Br (4c) 0.60300000000000 0.25000000000000 0.38100000000000 Br (4c) 0.61400000000000 0.25000000000000 0.84200000000000 Br (4c) -0.11400000000000 0.75000000000000 1.34200000000000 Br (4c) -0.61400000000000 0.75000000000000 -0.84200000000000 Br (4c) 1.11400000000000 0.25000000000000 -0.34200000000000 Br (4c) 0.81100000000000 0.25000000000000 0.10800000000000 Sr (4c) -0.31100000000000 0.75000000000000 0.60800000000000 Sr (4c) -0.81100000000000 0.75000000000000 -0.10800000000000 Sr (4c) 1.31100000000000 0.25000000000000 0.39200000000000 Sr (4c)