A3B_tI32_82_3g_g & a,c/a,x1,y1,z1,x2,y2,z2,x3,y3,z3,x4,y4,z4 --params=8.954,0.495711413893,0.0775,0.1117,0.2391,0.3649,0.0321,0.9765,0.1689,0.22,0.7524,0.2862,0.0487,0.4807 & I-4 S_{4}^{2} #82 (g^4) & tI32 & $D0_{e}$ & Ni3P & & S. Rundqvist and E. Hassler and L. Lundvik, Acta Chem. Scand. 16, 242-243 (1962) 1.00000000000000 -4.47700000000000 4.47700000000000 2.21930000000000 4.47700000000000 -4.47700000000000 2.21930000000000 4.47700000000000 4.47700000000000 -2.21930000000000 Ni P 12 4 Direct 0.35080000000000 0.31660000000000 0.18920000000000 Ni (8g) 0.12740000000000 0.16160000000000 -0.18920000000000 Ni (8g) -0.31660000000000 -0.12740000000000 0.03420000000000 Ni (8g) -0.16160000000000 -0.35080000000000 -0.03420000000000 Ni (8g) 1.00860000000000 1.34140000000000 0.39700000000000 Ni (8g) 0.94440000000000 0.61160000000000 -0.39700000000000 Ni (8g) -1.34140000000000 -0.94440000000000 -0.33280000000000 Ni (8g) -0.61160000000000 -1.00860000000000 0.33280000000000 Ni (8g) 0.97240000000000 0.92130000000000 0.38890000000000 Ni (8g) 0.53240000000000 0.58350000000000 -0.38890000000000 Ni (8g) -0.92130000000000 -0.53240000000000 0.05110000000000 Ni (8g) -0.58350000000000 -0.97240000000000 -0.05110000000000 Ni (8g) 0.52940000000000 0.76690000000000 0.33490000000000 P (8g) 0.43200000000000 0.19450000000000 -0.33490000000000 P (8g) -0.76690000000000 -0.43200000000000 -0.23750000000000 P (8g) -0.19450000000000 -0.52940000000000 0.23750000000000 P (8g)