A4B2C_tP14_136_i_g_b & a,c/a,x2,x3,y3 --params=7.004,0.536122215877,0.2201,0.092,0.3468 & P4_{2}/mnm D_{4h}^{14} #136 (bgi) & tP14 & None & Fe4Si2Zr & Fe4Si2Zr & Y. P. Yarmolyuk and L. A. Lysenko and E. I. Gladyshevsky, Dopov. Akad. Nauk Ukr. RSR, Ser. A 37, 281-284 (1975) 1.00000000000000 7.00400000000000 0.00000000000000 0.00000000000000 0.00000000000000 7.00400000000000 0.00000000000000 0.00000000000000 0.00000000000000 3.75500000000000 Fe Si Zr 8 4 2 Direct 0.09200000000000 0.34680000000000 0.00000000000000 Fe (8i) -0.09200000000000 -0.34680000000000 0.00000000000000 Fe (8i) 0.15320000000000 0.59200000000000 0.50000000000000 Fe (8i) 0.84680000000000 0.40800000000000 0.50000000000000 Fe (8i) 0.40800000000000 0.84680000000000 0.50000000000000 Fe (8i) 0.59200000000000 0.15320000000000 0.50000000000000 Fe (8i) 0.34680000000000 0.09200000000000 0.00000000000000 Fe (8i) -0.34680000000000 -0.09200000000000 0.00000000000000 Fe (8i) 0.22010000000000 -0.22010000000000 0.00000000000000 Si (4g) -0.22010000000000 0.22010000000000 0.00000000000000 Si (4g) 0.72010000000000 0.72010000000000 0.50000000000000 Si (4g) 0.27990000000000 0.27990000000000 0.50000000000000 Si (4g) 0.00000000000000 0.00000000000000 0.50000000000000 Zr (2b) 0.50000000000000 0.50000000000000 0.00000000000000 Zr (2b)