A4B3_oP56_62_8c_6c & a,b/a,c/a,x1,z1,x2,z2,x3,z3,x4,z4,x5,z5,x6,z6,x7,z7,x8,z8,x9,z9,x10,z10,x11,z11,x12,z12,x13,z13,x14,z14 --params=12.428,0.254103636949,1.64467331831,0.1939,0.2262,0.3843,0.8518,0.1218,0.6891,0.298,0.0835,0.4007,0.5269,0.0952,0.4665,0.2977,0.3863,0.0095,0.8272,0.2464,-0.027,0.4824,0.4186,0.3206,0.6371,0.0382,0.5805,0.0155,0.2745,0.1994,0.7941 & Pnma D_{2h}^{16} #62 (c^14) & oP56 & None & Mo4P3 & Mo4P3 & S. Rundqvist, Acta Chem. Scand. 19, 393-400 (1965) 1.00000000000000 12.42800000000000 0.00000000000000 0.00000000000000 0.00000000000000 3.15800000000000 0.00000000000000 0.00000000000000 0.00000000000000 20.44000000000000 Mo P 32 24 Direct 0.19390000000000 0.25000000000000 0.22620000000000 Mo (4c) 0.30610000000000 0.75000000000000 0.72620000000000 Mo (4c) -0.19390000000000 0.75000000000000 -0.22620000000000 Mo (4c) 0.69390000000000 0.25000000000000 0.27380000000000 Mo (4c) 0.38430000000000 0.25000000000000 0.85180000000000 Mo (4c) 0.11570000000000 0.75000000000000 1.35180000000000 Mo (4c) -0.38430000000000 0.75000000000000 -0.85180000000000 Mo (4c) 0.88430000000000 0.25000000000000 -0.35180000000000 Mo (4c) 0.12180000000000 0.25000000000000 0.68910000000000 Mo (4c) 0.37820000000000 0.75000000000000 1.18910000000000 Mo (4c) -0.12180000000000 0.75000000000000 -0.68910000000000 Mo (4c) 0.62180000000000 0.25000000000000 -0.18910000000000 Mo (4c) 0.29800000000000 0.25000000000000 0.08350000000000 Mo (4c) 0.20200000000000 0.75000000000000 0.58350000000000 Mo (4c) -0.29800000000000 0.75000000000000 -0.08350000000000 Mo (4c) 0.79800000000000 0.25000000000000 0.41650000000000 Mo (4c) 0.40070000000000 0.25000000000000 0.52690000000000 Mo (4c) 0.09930000000000 0.75000000000000 1.02690000000000 Mo (4c) -0.40070000000000 0.75000000000000 -0.52690000000000 Mo (4c) 0.90070000000000 0.25000000000000 -0.02690000000000 Mo (4c) 0.09520000000000 0.25000000000000 0.46650000000000 Mo (4c) 0.40480000000000 0.75000000000000 0.96650000000000 Mo (4c) -0.09520000000000 0.75000000000000 -0.46650000000000 Mo (4c) 0.59520000000000 0.25000000000000 0.03350000000000 Mo (4c) 0.29770000000000 0.25000000000000 0.38630000000000 Mo (4c) 0.20230000000000 0.75000000000000 0.88630000000000 Mo (4c) -0.29770000000000 0.75000000000000 -0.38630000000000 Mo (4c) 0.79770000000000 0.25000000000000 0.11370000000000 Mo (4c) 0.00950000000000 0.25000000000000 0.82720000000000 Mo (4c) 0.49050000000000 0.75000000000000 1.32720000000000 Mo (4c) -0.00950000000000 0.75000000000000 -0.82720000000000 Mo (4c) 0.50950000000000 0.25000000000000 -0.32720000000000 Mo (4c) 0.24640000000000 0.25000000000000 -0.02700000000000 P (4c) 0.25360000000000 0.75000000000000 0.47300000000000 P (4c) -0.24640000000000 0.75000000000000 0.02700000000000 P (4c) 0.74640000000000 0.25000000000000 0.52700000000000 P (4c) 0.48240000000000 0.25000000000000 0.41860000000000 P (4c) 0.01760000000000 0.75000000000000 0.91860000000000 P (4c) -0.48240000000000 0.75000000000000 -0.41860000000000 P (4c) 0.98240000000000 0.25000000000000 0.08140000000000 P (4c) 0.32060000000000 0.25000000000000 0.63710000000000 P (4c) 0.17940000000000 0.75000000000000 1.13710000000000 P (4c) -0.32060000000000 0.75000000000000 -0.63710000000000 P (4c) 0.82060000000000 0.25000000000000 -0.13710000000000 P (4c) 0.03820000000000 0.25000000000000 0.58050000000000 P (4c) 0.46180000000000 0.75000000000000 1.08050000000000 P (4c) -0.03820000000000 0.75000000000000 -0.58050000000000 P (4c) 0.53820000000000 0.25000000000000 -0.08050000000000 P (4c) 0.01550000000000 0.25000000000000 0.27450000000000 P (4c) 0.48450000000000 0.75000000000000 0.77450000000000 P (4c) -0.01550000000000 0.75000000000000 -0.27450000000000 P (4c) 0.51550000000000 0.25000000000000 0.22550000000000 P (4c) 0.19940000000000 0.25000000000000 0.79410000000000 P (4c) 0.30060000000000 0.75000000000000 1.29410000000000 P (4c) -0.19940000000000 0.75000000000000 -0.79410000000000 P (4c) 0.69940000000000 0.25000000000000 -0.29410000000000 P (4c)