A4BC2D_oP32_62_2cd_b_2c_a & a,b/a,c/a,x3,z3,x4,z4,x5,z5,x6,z6,x7,y7,z7 --params=12.05,0.755186721992,0.684647302905,-0.05,0.21,0.05,0.79,0.2,0.34,0.825,0.6,0.25,-0.04,0.12 & Pnma D_{2h}^{16} #62 (abc^4d) & oP32 & $E3_{5}$ & Cl4(H2O)K2Sn & Cl4(H2O)K2Sn & H. Brasseur and A. {de Rassenfosse}, Zeitschrift f{"u}r Kristallographie - Crystalline Materials 101, 389-395 (1939) 1.00000000000000 12.05000000000000 0.00000000000000 0.00000000000000 0.00000000000000 9.10000000000000 0.00000000000000 0.00000000000000 0.00000000000000 8.25000000000000 Cl H2O K Sn 16 4 8 4 Direct -0.05000000000000 0.25000000000000 0.21000000000000 Cl (4c) 0.55000000000000 0.75000000000000 0.71000000000000 Cl (4c) 0.05000000000000 0.75000000000000 -0.21000000000000 Cl (4c) 0.45000000000000 0.25000000000000 0.29000000000000 Cl (4c) 0.05000000000000 0.25000000000000 0.79000000000000 Cl (4c) 0.45000000000000 0.75000000000000 1.29000000000000 Cl (4c) -0.05000000000000 0.75000000000000 -0.79000000000000 Cl (4c) 0.55000000000000 0.25000000000000 -0.29000000000000 Cl (4c) 0.25000000000000 -0.04000000000000 0.12000000000000 Cl (8d) 0.25000000000000 0.04000000000000 0.62000000000000 Cl (8d) -0.25000000000000 0.46000000000000 -0.12000000000000 Cl (8d) 0.75000000000000 0.54000000000000 0.38000000000000 Cl (8d) -0.25000000000000 0.04000000000000 -0.12000000000000 Cl (8d) 0.75000000000000 -0.04000000000000 0.38000000000000 Cl (8d) 0.25000000000000 0.54000000000000 0.12000000000000 Cl (8d) 0.25000000000000 0.46000000000000 0.62000000000000 Cl (8d) 0.00000000000000 0.00000000000000 0.50000000000000 H2O (4b) 0.50000000000000 0.00000000000000 0.00000000000000 H2O (4b) 0.00000000000000 0.50000000000000 0.50000000000000 H2O (4b) 0.50000000000000 0.50000000000000 0.00000000000000 H2O (4b) 0.20000000000000 0.25000000000000 0.34000000000000 K (4c) 0.30000000000000 0.75000000000000 0.84000000000000 K (4c) -0.20000000000000 0.75000000000000 -0.34000000000000 K (4c) 0.70000000000000 0.25000000000000 0.16000000000000 K (4c) 0.82500000000000 0.25000000000000 0.60000000000000 K (4c) -0.32500000000000 0.75000000000000 1.10000000000000 K (4c) -0.82500000000000 0.75000000000000 -0.60000000000000 K (4c) 1.32500000000000 0.25000000000000 -0.10000000000000 K (4c) 0.00000000000000 0.00000000000000 0.00000000000000 Sn (4a) 0.50000000000000 0.00000000000000 0.50000000000000 Sn (4a) 0.00000000000000 0.50000000000000 0.00000000000000 Sn (4a) 0.50000000000000 0.50000000000000 0.50000000000000 Sn (4a)