A9B2C3_hP28_194_hk_f_bf & a,c/a,z2,z3,x4,x5,z5 --params=7.22,2.48337950139,0.837,0.077,0.508,0.824,0.092 & P6_{3}/mmc D_{6h}^{4} #194 (bf^2hk) & hP28 & None & Cl9Cr2Cs3 & Cl9Cr2Cs3 & G. G. Wessel and D. J. W. IJdo, Acta Cryst. 10, 466-468 (1957) 1.00000000000000 3.61000000000000 -6.25270341532365 0.00000000000000 3.61000000000000 6.25270341532365 0.00000000000000 0.00000000000000 0.00000000000000 17.93000000000000 Cl Cr Cs 18 4 6 Direct 0.50800000000000 1.01600000000000 0.25000000000000 Cl (6h) -1.01600000000000 -0.50800000000000 0.25000000000000 Cl (6h) 0.50800000000000 -0.50800000000000 0.25000000000000 Cl (6h) -0.50800000000000 -1.01600000000000 0.75000000000000 Cl (6h) 1.01600000000000 0.50800000000000 0.75000000000000 Cl (6h) -0.50800000000000 0.50800000000000 0.75000000000000 Cl (6h) 0.82400000000000 1.64800000000000 0.09200000000000 Cl (12k) -1.64800000000000 -0.82400000000000 0.09200000000000 Cl (12k) 0.82400000000000 -0.82400000000000 0.09200000000000 Cl (12k) -0.82400000000000 -1.64800000000000 0.59200000000000 Cl (12k) 1.64800000000000 0.82400000000000 0.59200000000000 Cl (12k) -0.82400000000000 0.82400000000000 0.59200000000000 Cl (12k) 1.64800000000000 0.82400000000000 -0.09200000000000 Cl (12k) -0.82400000000000 -1.64800000000000 -0.09200000000000 Cl (12k) -0.82400000000000 0.82400000000000 -0.09200000000000 Cl (12k) -1.64800000000000 -0.82400000000000 0.40800000000000 Cl (12k) 0.82400000000000 1.64800000000000 0.40800000000000 Cl (12k) 0.82400000000000 -0.82400000000000 0.40800000000000 Cl (12k) 0.33333333333333 0.66666666666667 0.83700000000000 Cr (4f) 0.66666666666667 0.33333333333333 1.33700000000000 Cr (4f) 0.66666666666667 0.33333333333333 -0.83700000000000 Cr (4f) 0.33333333333333 0.66666666666667 -0.33700000000000 Cr (4f) 0.00000000000000 0.00000000000000 0.25000000000000 Cs (2b) 0.00000000000000 0.00000000000000 0.75000000000000 Cs (2b) 0.33333333333333 0.66666666666667 0.07700000000000 Cs (4f) 0.66666666666667 0.33333333333333 0.57700000000000 Cs (4f) 0.66666666666667 0.33333333333333 -0.07700000000000 Cs (4f) 0.33333333333333 0.66666666666667 0.42300000000000 Cs (4f)