AB3C9D_hP28_173_a_c_3c_b & a,c/a,z1,z2,x3,y3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6 --params=8.84324,0.630487242232,0.358,0.25,0.3636,0.0854,0.2213,0.17,0.047,0.861,0.192,0.483,0.044,0.142,0.517,0.468 & P6_{3} C_{6}^{6} #173 (abc^4) & hP28 & None & BLa3O9W & BLa3O9W & J. Han et al., ACS Appl. Mater. Interfaces 10, 13660-13668 (2018) 1.00000000000000 4.42162000000000 -7.65847049176270 0.00000000000000 4.42162000000000 7.65847049176270 0.00000000000000 0.00000000000000 0.00000000000000 5.57555000000000 B La O W 2 6 18 2 Direct 0.00000000000000 0.00000000000000 0.35800000000000 B (2a) 0.00000000000000 0.00000000000000 0.85800000000000 B (2a) 0.36360000000000 0.08540000000000 0.22130000000000 La (6c) -0.08540000000000 0.27820000000000 0.22130000000000 La (6c) -0.27820000000000 -0.36360000000000 0.22130000000000 La (6c) -0.36360000000000 -0.08540000000000 0.72130000000000 La (6c) 0.08540000000000 -0.27820000000000 0.72130000000000 La (6c) 0.27820000000000 0.36360000000000 0.72130000000000 La (6c) 0.17000000000000 0.04700000000000 0.86100000000000 O (6c) -0.04700000000000 0.12300000000000 0.86100000000000 O (6c) -0.12300000000000 -0.17000000000000 0.86100000000000 O (6c) -0.17000000000000 -0.04700000000000 1.36100000000000 O (6c) 0.04700000000000 -0.12300000000000 1.36100000000000 O (6c) 0.12300000000000 0.17000000000000 1.36100000000000 O (6c) 0.19200000000000 0.48300000000000 0.04400000000000 O (6c) -0.48300000000000 -0.29100000000000 0.04400000000000 O (6c) 0.29100000000000 -0.19200000000000 0.04400000000000 O (6c) -0.19200000000000 -0.48300000000000 0.54400000000000 O (6c) 0.48300000000000 0.29100000000000 0.54400000000000 O (6c) -0.29100000000000 0.19200000000000 0.54400000000000 O (6c) 0.14200000000000 0.51700000000000 0.46800000000000 O (6c) -0.51700000000000 -0.37500000000000 0.46800000000000 O (6c) 0.37500000000000 -0.14200000000000 0.46800000000000 O (6c) -0.14200000000000 -0.51700000000000 0.96800000000000 O (6c) 0.51700000000000 0.37500000000000 0.96800000000000 O (6c) -0.37500000000000 0.14200000000000 0.96800000000000 O (6c) 0.33333333333333 0.66666666666667 0.25000000000000 W (2b) 0.66666666666667 0.33333333333333 0.75000000000000 W (2b)