AB6C2_oP36_62_c_2c2d_d & a,b/a,c/a,x1,z1,x2,z2,x3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6 --params=11.068,0.678080954102,0.485905312613,0.042,0.54,0.146,-0.033,0.878,0.838,-0.024,0.035,0.225,0.213,0.049,0.383,0.1412,-0.0056,0.0376 & Pnma D_{2h}^{16} #62 (c^3d^3) & oP36 & None & CaO6Ta2 & Rynersonite & L. Jahnberg, Acta Chem. Scand. 71, 2548-2559 (1963) 1.00000000000000 11.06800000000000 0.00000000000000 0.00000000000000 0.00000000000000 7.50500000000000 0.00000000000000 0.00000000000000 0.00000000000000 5.37800000000000 Ca O Ta 4 24 8 Direct 0.04200000000000 0.25000000000000 0.54000000000000 Ca (4c) 0.45800000000000 0.75000000000000 1.04000000000000 Ca (4c) -0.04200000000000 0.75000000000000 -0.54000000000000 Ca (4c) 0.54200000000000 0.25000000000000 -0.04000000000000 Ca (4c) 0.14600000000000 0.25000000000000 -0.03300000000000 O (4c) 0.35400000000000 0.75000000000000 0.46700000000000 O (4c) -0.14600000000000 0.75000000000000 0.03300000000000 O (4c) 0.64600000000000 0.25000000000000 0.53300000000000 O (4c) 0.87800000000000 0.25000000000000 0.83800000000000 O (4c) -0.37800000000000 0.75000000000000 1.33800000000000 O (4c) -0.87800000000000 0.75000000000000 -0.83800000000000 O (4c) 1.37800000000000 0.25000000000000 -0.33800000000000 O (4c) -0.02400000000000 0.03500000000000 0.22500000000000 O (8d) 0.52400000000000 -0.03500000000000 0.72500000000000 O (8d) 0.02400000000000 0.53500000000000 -0.22500000000000 O (8d) 0.47600000000000 0.46500000000000 0.27500000000000 O (8d) 0.02400000000000 -0.03500000000000 -0.22500000000000 O (8d) 0.47600000000000 0.03500000000000 0.27500000000000 O (8d) -0.02400000000000 0.46500000000000 0.22500000000000 O (8d) 0.52400000000000 0.53500000000000 0.72500000000000 O (8d) 0.21300000000000 0.04900000000000 0.38300000000000 O (8d) 0.28700000000000 -0.04900000000000 0.88300000000000 O (8d) -0.21300000000000 0.54900000000000 -0.38300000000000 O (8d) 0.71300000000000 0.45100000000000 0.11700000000000 O (8d) -0.21300000000000 -0.04900000000000 -0.38300000000000 O (8d) 0.71300000000000 0.04900000000000 0.11700000000000 O (8d) 0.21300000000000 0.45100000000000 0.38300000000000 O (8d) 0.28700000000000 0.54900000000000 0.88300000000000 O (8d) 0.14120000000000 -0.00560000000000 0.03760000000000 Ta (8d) 0.35880000000000 0.00560000000000 0.53760000000000 Ta (8d) -0.14120000000000 0.49440000000000 -0.03760000000000 Ta (8d) 0.64120000000000 0.50560000000000 0.46240000000000 Ta (8d) -0.14120000000000 0.00560000000000 -0.03760000000000 Ta (8d) 0.64120000000000 -0.00560000000000 0.46240000000000 Ta (8d) 0.14120000000000 0.50560000000000 0.03760000000000 Ta (8d) 0.35880000000000 0.49440000000000 0.53760000000000 Ta (8d)