AB8C4_mC52_12_i_gi3j_2j & a,b/a,c/a,beta,y1,x2,z2,x3,z3,x4,y4,z4,x5,y5,z5,x6,y6,z6,x7,y7,z7,x8,y8,z8 --params=8.595,1.51576497964,0.834787667248,115.94,0.147,0.2866,0.138,0.64,0.2849,0.8302,0.1476,0.2269,0.0351,0.3105,0.2569,0.1789,0.1265,0.4083,0.00991,0.1856,0.22381,0.71075,0.11813,0.34438 & C2/m C_{2h}^{3} #12 (gi^2j^5) & mC52 & $S6_{7}$ & AlKO8Si3 & Sanidine & T. A. Scambos and J. R. Smyth and T. C. {McCormick}, Am. Mineral. 72, 973-978 (1987) 1.00000000000000 4.29750000000000 -6.51400000000000 0.00000000000000 4.29750000000000 6.51400000000000 0.00000000000000 -3.13855803775329 0.00000000000000 6.45213750966718 K O Si 2 16 8 Direct 0.28660000000000 0.28660000000000 0.13800000000000 K (4i) -0.28660000000000 -0.28660000000000 -0.13800000000000 K (4i) -0.14700000000000 0.14700000000000 0.00000000000000 O (4g) 0.14700000000000 -0.14700000000000 0.00000000000000 O (4g) 0.64000000000000 0.64000000000000 0.28490000000000 O (4i) -0.64000000000000 -0.64000000000000 -0.28490000000000 O (4i) 0.68260000000000 0.97780000000000 0.22690000000000 O (8j) -0.97780000000000 -0.68260000000000 -0.22690000000000 O (8j) -0.68260000000000 -0.97780000000000 -0.22690000000000 O (8j) 0.97780000000000 0.68260000000000 0.22690000000000 O (8j) -0.27540000000000 0.34560000000000 0.25690000000000 O (8j) -0.34560000000000 0.27540000000000 -0.25690000000000 O (8j) 0.27540000000000 -0.34560000000000 -0.25690000000000 O (8j) 0.34560000000000 -0.27540000000000 0.25690000000000 O (8j) 0.05240000000000 0.30540000000000 0.40830000000000 O (8j) -0.30540000000000 -0.05240000000000 -0.40830000000000 O (8j) -0.05240000000000 -0.30540000000000 -0.40830000000000 O (8j) 0.30540000000000 0.05240000000000 0.40830000000000 O (8j) -0.17569000000000 0.19551000000000 0.22381000000000 Si (8j) -0.19551000000000 0.17569000000000 -0.22381000000000 Si (8j) 0.17569000000000 -0.19551000000000 -0.22381000000000 Si (8j) 0.19551000000000 -0.17569000000000 0.22381000000000 Si (8j) 0.59262000000000 0.82888000000000 0.34438000000000 Si (8j) -0.82888000000000 -0.59262000000000 -0.34438000000000 Si (8j) -0.59262000000000 -0.82888000000000 -0.34438000000000 Si (8j) 0.82888000000000 0.59262000000000 0.34438000000000 Si (8j)